Research Article
Published: 25 July, 2018 | Volume 2 - Issue 1 | Pages: 001-007
Objectives: To evaluate the colour stability of 3 recently developed resin based materials continuously exposed to various staining agents.
Methods: 144 disc-shaped specimens were made of each of the 3 tested composites (Essentia, Brillant, Inspiro). Half of them were of 1mm thickness, the other half 1.2mm thickness. The thicker group was than polished up to 4000 grit and reduced to 1mm thickness, too. All specimens after 24 h dry storage in an incubator (INP-500, Memmert), received an initial colour measurement by means of a calibrated reflectance spectrophotometer (SpectroShade, MHT, Niederhasli, Switzerland). Specimens were then divided into 6 groups (n=6) and immersed in 5 staining solutions or artificial saliva (control). All specimens were kept in an incubator at 37°C for 28 days. Staining solutions (red wine, curry mixed water, curry mixed oil, tea and coffee) were changed every 7th day to avoid bacteria or yeast contamination. After 28 days of storage spectrophotometric measurements were repeated and L*a*b* scores once more recorded to determine the colour (ΔE00) changes.
Results: All tested materials showed significant color changes after 28 days staining immersion.
When considered over a black background ΔE00 of polished samples varied from 1.7 (Brillant/distilled water) to 24.1 (Brillant/wine).
When considered over a white background ΔE00 of polished samples varied from 1.1 (Essentia/distilled water) to 32.5 (Inspiro/wine).
When considered over a black background ΔE00 of unpolished samples varied from 1.1 (Essentia, Inspiro/distilled water) to 25.8 (Essentia/wine).
When considered over a white background ΔE00 of unpolished samples varied from 1.4(Inspiro/distilled water) to 33.1 (Inspiro/wine).
Conclusions: Staining of restorative materials seems to be dependent on the composition of the product itself. Unpolished samples demonstrated to be more prone to staining than the polished ones
Read Full Article HTML DOI: 10.29328/journal.jcad.1001006 Cite this Article Read Full Article PDF
HSPI: We're glad you're here. Please click "create a new Query" if you are a new visitor to our website and need further information from us.
If you are already a member of our network and need to keep track of any developments regarding a question you have already submitted, click "take me to my Query."